Title of the article CORROSION-MECHANICAL FATIGUE: THE PROBLEMS OF FORECASTING. PART 3. MECHANISMS OF CORROSION-MECHANICAL FATIGUE
Authors

SOSNOVSKIY Leonid A., D. Sc. in Eng., Prof.

BOGDANOVICH Alexander V., D. Sc. in Eng., Prof., Professor of the Department of Theoretical and Applied Mechanics, Belarusian State University, Minsk, Republic of Belarus, This email address is being protected from spambots. You need JavaScript enabled to view it.">This email address is being protected from spambots. You need JavaScript enabled to view it.

TARANOVA Elena S., Lecturer of the Department “Locomotives”, Belarusian State University of Transport, Gomel, Republic of Belarus, This email address is being protected from spambots. You need JavaScript enabled to view it.">This email address is being protected from spambots. You need JavaScript enabled to view it.

In the section TRIBO-FATIGUE SYSTEMS MECHANICS
Year 2024
Issue 1(66)
Pages 86–94
Type of article RAR
Index UDK 620.178.3
DOI https://doi.org/10.46864/1995-0470-2024-1-66-86-94
Abstract Corrosion is one of the main electrochemical processes that damage metal materials. The combination of cyclic stresses and a corrosive environment causes wear-fatigue damage, called corrosion-mechanical fatigue. The paper investigates the problem of predicting this type of corrosion-fatigue damage, which occurs in almost all branches of technology, especially in the chemical, oil, metallurgical industries, transport. The work consists of several parts. In the first part a technique for estimating the fatigue limit in a given corrosive environment (direct effect) is developed. The second part analyzes the reverse effect, i.e. the effect of acting stresses on the corrosion rate of metals and alloys, and proposes a method for predicting corrosion-erosion damage with the reverse effect based on the energy criterion. The third part discusses the mechanisms of corrosion-mechanical fatigue with direct and reverse effects taking into account the interacting phenomena of adsorption, hydrogen and corrosion fatigue itself. The concept of diffuse effect of multiple shear, oxidation, transfer is introduced as a complex type of damage in corrosion-mechanical fatigue.
Keywords corrosion-mechanical fatigue, fatigue resistance, direct effect, reverse effect, cyclic stress, damage mechanisms
  You can access full text version of the article.
Bibliography
  1. Gutman E.М. Mekhanokhimiya metallov i zashchita ot korrozii [Mechanochemistry of metals and corrosion protection]. Moscow, Metallurgiya Publ., 1981. 270 p. (in Russ.).
  2. Pokhmurskiy V.I. Korrozionnaya ustalost metallov [Corrosion fatigue of metals]. Moscow, Metallurgiya Publ., 1985. 206 p. (in Russ.).
  3. The theory of stress corrosion cracking in alloys. Brussels, NATO Scientific Affairs Division, 1971. 321 р.
  4. Evans U.R. The corrosion and oxidation of metals: scientific principles and practical applications. London, Edward Arnold, 1960. 1094 p.
  5. Karpenko G.V. Vliyanie sredy na prochnost i dolgovechnost metallov [Influence of the medium on the strength and durability of metals]. Kiev, Nauchnaya mysl Publ., 1976. 127 p. (in Russ.).
  6. Romanov V.V. Vliyanie korrozionnoy sredy na tsiklicheskuyu prochnost metallov [Influence of a corrosive environment on the cyclic strength of metals]. Moscow, Nauka Publ., 1969. 219 p. (in Russ.).
  7. Azhogin F.F. Korrozionnoe rastreskivanie i zashchita vysokoprochnykh staley [Stress corrosion cracking and protection of high strength steel]. Moscow, Metallurgiya Publ., 1974. 256 p. (in Russ.).
  8. Oleynik N.V., Magdenko A.N., Sklyar S.P. Soprotivlenie ustalosti materialov i detaley mashin v korrozionnykh sredakh [Fatigue resistance of materials and machine parts in corrosive environments]. Kiev, Nauchnaya mysl Publ., 1987. 197 p. (in Russ.).
  9. McCafferty E. Introduction to corrosion science. New York, Springer, 2010. 302 p. DOI: https://doi.org/10.1007/978-1-4419-0455-3.
  10. Milella P.P. Fatigue and corrosion in metals. Milano, Springer, 2012. 844 р. DOI: https://doi.org/10.1007/978-88-470-2336-9.
  11. Bache M., Ball C., Hardy M., Mignanelli P. Corrosion fatigue and damage tolerance in the nickel-based superalloy RR1000 subjected to SO2 environments. Fatigue & fracture engineering materials & structures, 2022, vol. 45, iss. 5, pp. 1537–1549. DOI: https://doi.org/10.1111/ffe.13687.
  12. McMahon M.E. Review of residual stress impingement methods to mitigate environmental fracture susceptibility. Corrosion and materials degradation, 2021, vol. 2, iss. 4, pp. 582–602. DOI: https://doi.org/10.3390/cmd2040031.
  13. Xue S., Shen R. Corrosion-fatigue analysis of high-strength steel wire by experiment and the numerical simulation. Metals, 2020, vol. 10, iss. 6. DOI: https://doi.org/10.3390/met10060734.
  14. Marandi L., Sen I. Effect of saline atmosphere on the mechanical properties of commercial steel wire. Metallurgical and materials transactions A, 2019, vol. 50, iss. 1, pp. 132–141. DOI: https://doi.org/10.1007/s11661-018-4956-x.
  15. Wang Y., Zheng Y. Research on corrosion fatigue performance and multiple fatigue sources fracture process of corroded steel wires. Advances in civil engineering, 2019, vol. 2019. DOI: https://doi.org/10.1155/2019/4914359.
  16. Sosnovskiy L.A. Tribofatika: problemy i perspektivy [Tribo-fatigue: problems and prospects]. Materialy tematicheskoy vystavki AN SSSR “Matematika i mekhanika — narodnomu khozyaystvu” [Proc. Thematic exhibition of the Academy of Sciences of the USSR “Mathematics and mechanics – to the national economy”]. Gomel, 1989, 63 p. (in Russ.).
  17. Sosnovskiy L.A. O mekhanicheskoy aktivatsii korrozionnykh protsessov pri tsiklicheskom nagruzhenii [On mechanical activation of corrosion processes under cyclic loading]. Tezisy dokladov mezhrespublikanskoy nauchno-tekhnicheskoy konferentsii “Povyshenie nadezhnosti i dolgovechnosti mashin i sooruzheniy” [Abstracts of papers of interrepublican scientific and technical conference “Improving the reliability and durability of machines and structures”]. Kiev, 1991, pp. 83–84 (in Russ.).
  18. Sosnovskiy L.A., Makhutov N.A. Tribofatika: iznosoustalostnye povrezhdeniya v problemakh resursa i bezopasnosti mashin [Tribo-fatigue: wear-fatigue damage in the problems of lifetime and safety of machines]. Moscow–Gomel, NPO “TRIBOFATIKA” Publ., FTsNTP “Bezopasnost” Publ., 2000. 304 p. (in Russ.).
  19. Sosnovskiy L.A, Bogdanovich A.V., Sherbakov S.S. Korrozionno-mekhanicheskaya ustalost: problemy prognozirovaniya. Chast 1. Pryamoy effekt [Corrosion-mechanical fatigue: the problems of forecasting. Part 1. Direct effect]. Mechanics of machines, mechanisms and materials, 2018, no. 1(42), pp. 51–57 (in Russ.).
  20. Sosnovskiy L.A., Bogdanovich A.V., Sherbakov S.S. Korrozionno-mekhanicheskaya ustalost: problemy prognozirovaniya. Chast 2. Obratnyy effekt. Vliyanie napryazheniy na skorost korrozii [Corrosion-mechanical fatigue: the problems of forecasting. Part 2. Reverse effect. Influence of stresses on the corrosion rate]. Mechanics of machines, mechanisms and materials, 2023, no. 2(63), pp. 61–68. DOI: https://doi.org/10.46864/1995-0470-2023-2-63-61-68 (in Russ.).
  21. Pokhmurskiy V.I., et al. O vliyanii nekotorykh pokrytiy na ustalostnuyu i korrozionno-ustalostnuyu prochnost stali Kh17N2 [On the effect of some coatings on the fatigue and corrosion-fatigue strength of steel Х17Н2 (Kh17N2)]. Fiziko-khimicheskaya mekhanika materialov, 1965, no. 6, pp. 694–696 (in Russ.).
  22. Parkins R.N. Predictive approaches to stress corrosion cracking failure. Corrosion science, 1980, vol. 20, iss. 2, pp. 147–166. DOI: https://doi.org/10.1016/0010-938X(80)90128-6.
  23. Devine Т.М. Corrosion of iron-base alloys. Treatise on materials science & technology, 1983, vol. 25, pp. 201–234. DOI: https://doi.org/10.1016/B978-0-12-341825-8.50012-X.
  24. Nelson H.G. Hydrogen embrittlement. Treatise on materials science & technology, 1983, vol. 25, pp. 275–359. DOI: https://doi.org/10.1016/B978-0-12-341825-8.50014-3.
  25. Romaniv O.N., Nikiforchin G.N. Mekhanika korrozionnogo razrusheniya konstruktsionnykh splavov [Corrosion fracture mechanics of structural alloys]. Moscow, Metallurgiya Publ., 1986. 293 p. (in Russ.).
  26. Glikman L.A. Korrozionno-mekhanicheskaya prochnost metallov [Corrosion-mechanical strength of metals]. Moscow–Leningrad, Mashgiz Publ., 1955. 176 p. (in Russ.).
  27. Corrosion fatigue: chemistry, mechanics and microstructure. Houston, National Association of Corrosion Engineers, 1972. 780 p.
  28. Ryabchenkov A.V. Korrozionno-ustalostnaya prochnost stali [Corrosion-fatigue strength of steel]. Moscow, Mashgiz Publ., 1953. 180 p. (in Russ.).
  29. Bogdanovich P.N., Prushak V.Ya. Trenie i iznos v mashinakh [Friction and wear in machines]. Minsk, Vysshaya shkola Publ., 1999. 374 p. (in Russ.).